ABS High Performance Black Flame Retardant Masterbatch (FR-ABS300H)

Original
price: Negotiable
minimum:
Total supply:
Delivery term: The date of payment from buyers deliver within days
seat: Beijing
Validity to: Long-term effective
Last update: 2017-09-24 01:18
Browse the number: 394
inquiry
Company Profile
 
 
Product details

Introduction

HXFR-ABS300 consists of environment friendly flame retardant system of bromine and antimony, passed the evaluation of SGS, CTI etc certification authority and comply with ROHS requirement. Advantage: high UV-Resistance, Non-blooming.

Application

Mainly used in black ABS injection and extrusion, such as: Panel, enclosure, frame of electric product and outer panel, Interior board, dashboard of automobile.

Index

Name

FR-ABS300H

Appearance

Black Granular

Content wt%>

74

Density g/cm3

2.0

Solubility Index g/min,200℃5kg

8.3

Decomposition Temp ℃≥

240

Water Content wt%≤

0.1

Melting Temp ℃≥

140

Extrusion Process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40.

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight.

Appendix:Application Examples

1-1.Formula

Materials

Formula A

Formula B

Formula C

Tianjin Dagu ABS417

78

80

75

HXFR-ABS300

22



HXFR-ABC302


20


HXFR-ABS303



25

1-2.Technical Data

Properties

Test Methods

Unit

ABS417

Formula A

Formula B

Formula C

Density

ASTMD-792

g/cm3

1.05

1.15

1.17

1.15

Melt Index

ASTMD-1238

g/10min

15.5




Tensile Strength

ASTM-D638

MPa

510

38.5

37.4

39.7

Elongation At Break

ASTM-D638

%

40

21.8

6.9

6.5

Flexural Strength

ASTM-D790

MPa

77

59.2

57.7

61.5

Flexural Modulus

ASTM-D790

MPa

25180

1900.4

2007.7

1875.3

Izod Impact Strength Notched(23℃)

ASTM-D256

KJ/m2

27

12.6

10.1

20.7

Flame Retardancy 3.2mm

UL94

‐‐

Non flame retardant

V0

V0

V0

CTI

IEC60695

GWFI:850/3.0

‐‐

Pass

Pass

Pass

Color



Natural color

Natural color

Natural color

Natural color

Note: the properties of HXFR-ABS300H are similar to HXFR-ABS300.

1-3. Injection Process:

Drying condition: Drying at 70-75 deg C to 2-3 hours by desiccant dryers.

Injection machine temperature setup:

Heating Zone

Step1

Step2

Step3

Nozzle

Temperature

205

210

220

200

All the application typical data above are just for reference, not an official warranty certificate. We provide different design solutions according to requirement of customers.

 